Specification
Brand : TGB
BulletPoint1 : D266 is a high manganese steel surfacing electrode with low hydrogen potassium type coating and added Molybdenum ato increases the wear and crack resistance
BulletPoint2 : Weld metal hardness, (all weld metal): HB ? 170
BulletPoint3 : Min AC OCV: 70 - Polarity: AC, DC +
BulletPoint4 : Application?Used for surfacing welding on abrasion parts of all kinds of crushers, high-manganese steel rails, buckets, bulldozers, etc
BulletPoint5 : You will receive 11 Lb of 14"L x Ø1/8" Electrodes
Color : S28-A-15-S 10 PCS
ExternallyAssignedProductIdentifier1 : 0600136283249
ExternallyAssignedProductIdentifier2 : 600136283249
FinishType : Finish
IncludedComponents : inc
ItemDisplayWeight : 11.2 pounds
ItemName : EFeMn-B - Hardfacing Low Hidrogen High Manganese Electrode - D266 - AWS 5.13-14" x 1/8" - (11 LBS)
ItemPackageDimensions_Height : 10 centimeters
ItemPackageDimensions_Length : 18 centimeters
ItemPackageDimensions_Width : 12 centimeters
ItemPackageQuantity : 1
ItemTypeKeyword : arc-welding-stick-electrodes
Manufacturer : TGB
Material : Iron
ModelName : DHKTBKNKD-1.6MM-GOLD
ModelNumber : DHKTBKNKD-1.6MM-GOLD
NumberOfBoxes : 1
NumberOfItems : 1
PartNumber : D266
Pattern : 1/8"
PowerSourceType : PowerSource
ProductDescription : Introduction: D266 is a high manganese steel surfacing electrode with low hydrogen potassium type coating AC/DC+ . (When AC welding, Open circuit (no load) voltages of arc welding should be higher than 70V). When surfacing use low current, narrow bead, hammer or water quench immediately when hot to reduce crack tendency. Use in austenitic high manganese steel. Due to the appropriate quantity of Molybdenum added to the weld, it increases the wear and crack resistance. Recommendations for welding: High manganese steels, in as cast condition or as weld metal, are sensitive to hot shortness and may crack if subjected to excessive heat. Under normal conditions the base material should not be preheated and interpass temperatures above 200 °C should be avoided. Welding outdoor in very cold weather, the base material should be warmed up to 50-100 °C. Weld metal hardness, (all weld metal): HB ? 170 Machinability: Grinding is normally applied. Overheating must be avoided. Redrying the electrodes: 200 °C, 2 h.