BulletPoint1 : LFB (bare low fuming bronze) is a general purpose oxyacetylene/brazing rod used for joining various ferrous and non-ferrous metals such as carbon steel, copper alloys, cast iron, malleable iron, stainless steel and some nickel alloys. Mechanical and physical characteristics include ductility, machineability, high strength, free flowing with good tinning action and a low melting point (1630°F)
BulletPoint2 : A “must have” filler metal for every machine shop, LFB is excellent for building up wearing surfaces or large areas where successive layers must be added; galvanized parts can be brazed without damaging the zinc coating. Precise balance of copper and zinc along with alloying elements of tin, iron, manganese and silicon produces weld deposits that can be easily machined but work harden once put into service; high silicon level promotes low fuming
BulletPoint3 : ***READ THIS: Main image is for reference only. Please check Picture #2 for an approximate quantity of rods per pound***
BulletPoint4 : Available in different sizes: 0.045", 1/6", 3/32", 1/8", 5/32", 3/16" and 1/4"
BulletPoint5 : Available in different package weights: 1 Lb, 2 Lb, 5 Lb and 10 Lb
Color : Blue
ExternallyAssignedProductIdentifier : 00840338553508
ExternallyAssignedProductIdentifier1 : 703856605398
ExternallyAssignedProductIdentifier2 : 0703856605398
ExternallyAssignedProductIdentifier3 : 00652426004508
IncludedComponents : 60 Sticks Brazing Rods
ItemDisplayWeight : 10 pounds
ItemName : RBCuZn-C - LFB Bare Bronze Brazing Rod - 36" x 3/32" (10 Lb)
ItemPackageDimensions_Height : 1.2 inches
ItemPackageDimensions_Length : 10.2 inches
ItemPackageDimensions_Width : 1.2 inches
ItemPackageQuantity : 1
ItemTypeKeyword : brazing-rods
Manufacturer : TGB
Material : Bronze
Material1 : iron
Material2 : metal
ModelName : Brazing Rods
ModelNumber : RBCuZn-C
NumberOfBoxes : 1
NumberOfItems : 60
NumberOfPieces : 1
PackageLevel : unit
PartNumber : LFB10x332_10
PowerSourceType : fire
ProductDescription : Recommended Braze-Welding Procedure: Preheating is recommended for some applications, however, overheating should be avoided. Voids may be formed in the joint by entrapped zinc vapors. Bevel cracks or heavy sections. Clean the area to be brazewelded as thoroughly as possible. Joint clearances of 0.002” – 0.005” (0.05 – 0.13mm) are suitable. Using a slightly oxidizing flame, preheat the part to be brazed. If using LFB, dip the rod into the bronze brazing flux (there is no need for more flux if using LFBFC) and then back to the area being brazed, while keeping the torch in constant motion to avoid overheating. The molten drops of LFB or LFBFC will follow the heat of the torch flame. Repeat the process until the joint is filled (Note: A benefit to using LFBFC over LFB is that it is not necessary to remove flux residue between passes). Allow the part to cool slowly before removing any slag, then use a wire brush to bring out a nice yellow brass color.
ProductSiteLaunchDate : 2016-09-22T15:20:53.008Z
Size : 3/32" - (10 Lb)
Style : 1#Tube
SupplierDeclaredDgHzRegulation : not_applicable
SupplierDeclaredHasProductIdentifierExemption : 1
UnitCount : 60
UnspscCode : 23271800