Specification
Brand : Blue Demon
BulletPoint1 : It is also used to repair castings
BulletPoint2 : With the high nickel content, the interposes temperature of not less than 350 degrees F is recommended during welding
BulletPoint3 : Welding current DCEP, AWS A5.15
BulletPoint4 : This rod can be used in all positions on AC or DC with a reverse polarity connection (DCEP)
BulletPoint5 : Yield Strength: ksi 94 Tensile Strength: ksi 132, Tensile Strength as work hardened: ksi 186
ExternallyAssignedProductIdentifier : 00840338553782
ExternallyAssignedProductIdentifier1 : 652426592425
ExternallyAssignedProductIdentifier2 : 0652426592425
ExternallyAssignedProductIdentifier3 : 00652426592425
IncludedComponents : WELDING ELECTRODE
ItemDisplayWeight : 0.64 pounds
ItemName : Blue Demon ENi-Cl 99 X 3/32" X 14" X 5LB pack Nickel 99 cast iron welding electrode
ItemPackageDimensions_Height : 5.08 centimeters
ItemPackageDimensions_Length : 31.242 centimeters
ItemPackageDimensions_Width : 6.096 centimeters
ItemPackageQuantity : 1
ItemTypeKeyword : brazing-rods
Manufacturer : Blue Demon
Material : nickel
ModelName : ENI99-332-05
ModelNumber : ENI99-332-05
NumberOfBoxes : 1
NumberOfItems : 1
PackageLevel : unit
PartNumber : ENI99-332-05
PowerSourceType : DCEP
ProductDescription : Recommended Braze-Welding Procedure: Preheating is recommended for some applications, however, overheating should be avoided. Voids may be formed in the joint by entrapped zinc vapors. Bevel cracks or heavy sections. Clean the area to be brazewelded as thoroughly as possible. Joint clearances of 0.002” – 0.005” (0.05 – 0.13mm) are suitable. Using a slightly oxidizing flame, preheat the part to be brazed. If using LFB, dip the rod into the bronze brazing flux (there is no need for more flux if using LFBFC) and then back to the area being brazed, while keeping the torch in constant motion to avoid overheating. The molten drops of LFB or LFBFC will follow the heat of the torch flame. Repeat the process until the joint is filled (Note: A benefit to using LFBFC over LFB is that it is not necessary to remove flux residue between passes). Allow the part to cool slowly before removing any slag, then use a wire brush to bring out a nice yellow brass color.