Specification
Brand : Blue Demon
BulletPoint1 : The welds are strong, dense and free of porosity on both production and maintenance applications
BulletPoint2 : 6000 is a great choice when welding heat-treated aluminum parts
BulletPoint3 : This rod may also be used in brazing applications
BulletPoint4 : This rod can be used in all positions on AC or DC with a reverse polarity connection (DCEP)
BulletPoint5 : Yield Strength: ksi 94 Tensile Strength: ksi 132, Tensile Strength as work hardened: ksi 186
ExternallyAssignedProductIdentifier : 00840338553782
ExternallyAssignedProductIdentifier1 : 652426006113
ExternallyAssignedProductIdentifier2 : 0652426006113
ExternallyAssignedProductIdentifier3 : 00652426006113
IncludedComponents : WELDING ELECTRODE
ItemDisplayWeight : 0.64 pounds
ItemName : Blue Demon Alloy 6000 X 1/8" X 14" X 5LB pack general purpose aluminum maintenance electrode
ItemPackageDimensions_Height : 7.112 centimeters
ItemPackageDimensions_Length : 36.576 centimeters
ItemPackageDimensions_Width : 7.62 centimeters
ItemPackageQuantity : 1
ItemTypeKeyword : brazing-rods
Manufacturer : Blue Demon
Material : aluminum
ModelName : ENI99-332-05
ModelNumber : BD-6000-125-05
NumberOfBoxes : 1
NumberOfItems : 1
PackageLevel : unit
PartNumber : BD-6000-125-05
PowerSourceType : DCEP
ProductDescription : Recommended Braze-Welding Procedure: Preheating is recommended for some applications, however, overheating should be avoided. Voids may be formed in the joint by entrapped zinc vapors. Bevel cracks or heavy sections. Clean the area to be brazewelded as thoroughly as possible. Joint clearances of 0.002” – 0.005” (0.05 – 0.13mm) are suitable. Using a slightly oxidizing flame, preheat the part to be brazed. If using LFB, dip the rod into the bronze brazing flux (there is no need for more flux if using LFBFC) and then back to the area being brazed, while keeping the torch in constant motion to avoid overheating. The molten drops of LFB or LFBFC will follow the heat of the torch flame. Repeat the process until the joint is filled (Note: A benefit to using LFBFC over LFB is that it is not necessary to remove flux residue between passes). Allow the part to cool slowly before removing any slag, then use a wire brush to bring out a nice yellow brass color.