Brand : Blue Demon
BulletPoint1 : E7018AC coating is formulated to work best on AC power source
BulletPoint2 : It is recommended for welding medium grade carbon steels where no preheat is used
BulletPoint3 : Typical applications include low-alloy structurals, low, medium and high carbon steels, offshore rigs and power plants
BulletPoint4 : This rod can be used in all positions on AC or DC with a reverse polarity connection (DCEP)
BulletPoint5 : Yield Strength: ksi 94 Tensile Strength: ksi 132, Tensile Strength as work hardened: ksi 186
ExternallyAssignedProductIdentifier : 00840338553782
ExternallyAssignedProductIdentifier1 : 652426532766
ExternallyAssignedProductIdentifier2 : 0652426532766
ExternallyAssignedProductIdentifier3 : 00652426532766
IncludedComponents : Welding Electrodes
ItemDisplayWeight : 0.64 pounds
ItemName : Blue Demon 7018AC X 5/32" X 14" X 5LB Plastic Low Hydrogen AC Welding Electrode
ItemPackageDimensions_Height : 5.08 centimeters
ItemPackageDimensions_Length : 36.068 centimeters
ItemPackageDimensions_Width : 5.588 centimeters
ItemPackageQuantity : 1
ItemTypeKeyword : brazing-rods
Manufacturer : Blue Demon
Material : high_carbon_steel
ModelName : E7018AC-532-05P
ModelNumber : E7018AC-532-05P
NumberOfBoxes : 1
NumberOfItems : 1
PackageLevel : unit
PartNumber : E7018AC-532-05P
PowerSourceType : AC-DCEP-DCEN
ProductDescription : Recommended Braze-Welding Procedure: Preheating is recommended for some applications, however, overheating should be avoided. Voids may be formed in the joint by entrapped zinc vapors. Bevel cracks or heavy sections. Clean the area to be brazewelded as thoroughly as possible. Joint clearances of 0.002” – 0.005” (0.05 – 0.13mm) are suitable. Using a slightly oxidizing flame, preheat the part to be brazed. If using LFB, dip the rod into the bronze brazing flux (there is no need for more flux if using LFBFC) and then back to the area being brazed, while keeping the torch in constant motion to avoid overheating. The molten drops of LFB or LFBFC will follow the heat of the torch flame. Repeat the process until the joint is filled (Note: A benefit to using LFBFC over LFB is that it is not necessary to remove flux residue between passes). Allow the part to cool slowly before removing any slag, then use a wire brush to bring out a nice yellow brass color.
ProductSiteLaunchDate : 2013-10-21T00:00:01-07:00
Size : 5/32"(Diameter)
Style : 5# Plastic
SupplierDeclaredDgHzRegulation : not_applicable
UnitCount : 1
UnspscCode : 23271800